Magnesium Alloy Suppliers Rod Metal Products Dissolvable Magnesium
Alloy Bar
Introduction:
The weldability of most magnesium alloys is good when proper filler
metal in employed. A filler metal with a lower melting point and a
wider freezing range than the base metal will provide good
weldability and minimize weld cracking. AZ61A or AZ92A filler
metals may be used to weld base metals of similar composition and
also ZK21A base metal.
AZ61A filler metal is generally preferred for welding wrought base
metals of those alloys because of lower cracking tendency. However,
welds made in cast Mg-Al-Zn and AM100A base metals with AZ92A
filler metal show less crack sensitivity. The weld metal will
respond to the precipitation heat treatments normally applied to
repaired castings. AZ101A filler metal may also be used to weld
those cast base metals. EZ33A filler metal is used to weld wrought
and cast base metals designed for elevated-temperature service;
however, this filler metal should not be used for welding
aluminum-bearing magnesium alloys because of severe weld cracking
problems. When no other filler metal is available, most base metals
may be welded with strips cut from the base metal.
Parameter:
| |
| 300mm or as customer's required |
| 900.0mm or as customer's required |
| 2000mm or as customer's required |
| 1000*2000mm,1219*2438mm,1219*3048mm,or as customer's required |
| Carving,aerospace,auto,concrete tools,3C(cell
phone/camera/compute),water heater,refrigerator,gas pipelines etc. |
| 1.Good resistance to deformation force |
|
3.Good absorption of vibration energy performance |
4.Good impact energy absorption characteristics |
5.Low melting, small specific heat |
| Ordinary industrial surface,or customized |
| |
| loy Element | Type | Chemical Composition% | Other elements b |
| Mg | Al | Zn | Mn | Ce | Zr | Si | Fe | Ca | Cu | Ni | Be | Sub-total | total |
| MgAlZn | AZ31B | Balance | 2.5-3.5 | 0.6-1.4 | 0.1-0.2 | --- | --- | ≤0.08 | ≤0.003 | ≤0.04 | ≤0.01 | ≤0.001 | --- | ≤0.05 | ≤0.30 |
| AZ40M | Balance | 3.0-4.0 | 0.2-0.8 | 0.15-0.5 | --- | --- | ≤0.10 | ≤0.05 | --- | ≤0.05 | ≤0.005 | ≤0.01 | ≤0.01 | ≤0.30 |
| AZ80A | Balance | 7.8-9.2 | 0.2-0.8 | 0.12-0.5 | --- | --- | ≤0.10 | ≤0.005 | --- | ≤0.05 | ≤0.005 | --- | --- | ≤0.30 |
| AZ91D | Balance | 8.5-9.5 | 0.45-0.9 | 0.17-0.4 | --- | --- | ≤0.08 | ≤0.004 | --- | ≤0.025 | ≤0.001 | 0.0005- | ≤0.01 | ≤0.30 |
| 0.003 |
| MgMn | M2M | Balance | ≤0.20 | ≤0.30 | 1.3-2.5 | --- | --- | ≤0.10 | ≤0.05 | --- | ≤0.05 | ≤0.007 | ≤0.01 | ≤0.01 | ≤0.20 |
| MgZnZr | ZK61M | Balance | ≤0.05 | 5.0-6.0 | ≤0.10 | --- | 0.3-0.9 | ≤0.05 | ≤0.05 | --- | ≤0.05 | ≤0.005 | ≤0.01 | ≤0.01 | ≤0.30 |
| MgMnRe | ME20M | Balance | ≤0.20 | ≤0.30 | 1.32-2.2 | 0.15-0.35 | --- | ≤0.10 | ≤0.05 | --- | ≤0.05 | ≤0.007 | ≤0.01 | ≤0.01 | ≤0.30 |
Application:Mg alloy sacrificial anodes are suitable for the anti-corrosion
protection of such projects are oil pipelines, gas pipelines, water
supply pipes and drain-pipes, underground cables, chemical plants,
communication, harbors, watercrafts and reservoir strobe.
Standard:ASTM B843-1995,GB/T21448-2008,GB/T17731-2009
Production-Quality Control
Quality Control in our foundry begins on the foundry floor, where
the first line of inspection is the casting and molding crew, our
lab technicians inspectors and managers completes the quality team.
Our quality control staff carefully monitors raw material, core
materials,packaging and all aspects of production.